无机材料填充改性PTFE复合材料研究进展

综述了聚四氟乙烯（PTFE）无机材料填充改性中纤维填充改性，颗粒填充改性以及复合填充改性三大类的改性研究进展。介绍了不同无机填料对于PTFE复合材料的力学性能以及摩擦学性能的影响，包括摩擦因数、拉伸强度以及材料硬度等，发现铜（Cu）粉、二硫化钼（MoS2）以及玻璃纤维（GF）等无机填料成本较低且对PTFE的力学性能以及摩擦学性能改善较为明显，更能满足实际工程应用。最后，分析了国内外近年来研究中所存在的问题，并提出了解决方向。     

Reducing the power consumption of household refrigerators through the integration of latent heat storage elements in wire-and-tube condensers

This study evaluates the influence of latent heat storage elements on the condenser temperature of a commercial household refrigerator. In order to determine the power consumption and the temperature distribution, a standard wire-and-tube condenser is equipped with different heat storage elements (containing water, paraffin or copolymer compound). The results indicate that particularly the application of phase change materials (PCM) lowers the condenser temperature, which leads to a significantly reduced power consumption.     

PZT components derived from polysulphone spinning process

The present paper deals with the development of lead zirconate titanate (PZT) fibres, pearls and fibre fragments, for their use as active phase in piezocomposites. As new a approach, the green ceramic components are shaped by polysulphone spinning, allowing for effective and flexible forming over a wide range of different geometries and sizes. The correlation between processing parameters, e.g. the slurry composition, nozzle size and operation velocity, and the resultant shape of ceramic components is analysed. Sintered piezoceramic parts show a dense microstructure. Performance data are evaluated on PZT/epoxy composites. Measurement results of strain, polarisation and piezoelectric coupling are given and discussed. The developed PZT components are seen as key for the creation of smart and lightweight structural components. Further, free formed PZT components open new design approaches for sensing and actuating devices and ultrasound transducers.     

FeO0.7F1.3/C Nanocomposite as a High‐Capacity Cathode Material for Sodium‐Ion Batteries

Searching high capacity cathode materials is one of the most important fields of the research and development of sodium‐ion batteries (SIBs). Here, we report a FeO_0.7F_1.3/C nanocomposite synthesized via a solution process as a new cathode material for SIBs. This material exhibits a high initial discharge capacity of 496 mAh g^?1 in a sodium cell at 50 °C. From the 3^rd to 50^th cycle, the capacity fading is only 0.14% per cycle (from 388 mAh g^?1 at 3^rd the cycle to 360 mAh g^?1 at the 50^th cycle), demonstrating superior cyclability. A high energy density of 650 Wh kg^?1 is obtained at the material level. The reaction mechanism studies of FeO_0.7F_1.3/C with sodium show a hybridized mechanism of both intercalation and conversion reaction.     

基于源质的煤基中间相小球体生成与可控演化

煤全组分族分离所得的密中质组是中间相小球体生成的来源物质（即源质）。以该源质为原料，制备煤基碳质中间相。考察了炭化过程中温度、恒温时间、氮气流速、原料进样方式和添加剂等因素对中间相小球体生成过程的影响，探讨了中间相小球体演化过程的可控性。结果表明：温度、恒温时间、进样方式是影响中间相小球体生成的主要因素，能够控制生成中间相小球体粒径大小；温度升高或恒温时间延长均会加剧原料分子的热反应，促进中间相小球体的生成和融并；大面积的融并将使粒度迅速增加，部分球体解体，球体数目下降，最终形成体中间相；进样方式主要通过影响小球体演化过程中挥发性气体的逸出及原料颗粒间热传递效率影响小球体的生成和发展；氮气流速起到辅助调控作用；添加剂的加入促进了原料成核，加速了小球体的生成。     

Enhanced Oxidative Desulfurization of Dibenzothiophene by Functional Mo‐Containing Mesoporous Silica

Functional mesoporous Mo–SiO₂ materials were synthesized by a one‐pot and facile room‐temperature procedure, and characterized by X‐ray diffraction, TEM, Raman spectroscopy, FT‐IR, diffuse reflectance spectra, and BET analysis. The experimental results demonstrated that the mesoporous materials presented a high dispersion of molybdenum species and excellent catalytic activity for the removal of dibenzothiophene (DBT) without organic solvents as extractants. The catalytic performance on different sulfur‐containing compounds was also investigated in detail. After recycling for eight times, the removal of the oxidation desulfurization system could still reach high values. GC‐MS analysis detected the oxidation product of DBT. A mechanism was proposed for the absorptive oxidation process of sulfur compounds.     

凉感纤维织物导热系数影响因素的探讨

采用普通涤纶、含1%云母颗粒的涤纶(1%云母/涤纶)以及含5%云母颗粒的涤纶(5%云母/涤纶)三种材质,上机纬密采用200根/10 cm、300根/10 cm、400根/10 cm,组织采用平纹、斜纹、缎纹试织试样。通过Hot Disk热常数分析仪,采用正交试验及极差、方差分析,研究了纤维材质、上机纬密、组织对凉感纤维织物导热系数的影响。结果表明:在试验设置变量范围内,纤维材质对导热系数的影响显著,上机纬密、组织对导热系数的影响高度显著,影响因素从大到小顺序为上机纬密>组织>纤维材质。     

光伏废料制备Si3N4-SiC材料的抗氧化性和抗侵蚀性

将光伏废料经酸洗除杂后,与硅粉按85∶15的质量比配料,以聚乙二醇做结合剂,成型为10 mm×10 mm×20 mm的生坯后,在1380℃保温2 h氮化制成Si3N4-SiC材料,然后研究了该Si3N4-SiC材料的抗氧化性和抗侵蚀性。结果表明:1)制备的Si3N4-SiC材料在空气气氛中抗氧化性较好,主要是由于其氧化产物Si2N2O和SiO2填充气孔,促进烧结,提高了试样的致密度。2)在静态熔盐(Na3AlF6)中的抗侵蚀性能较好,主要是由于Na3AlF6渗入气孔中,使其显气孔率降低。3)在动态熔盐中的抗侵蚀性相对变差,主要是由于CO2气体的搅拌和对Si3N4、SiC的氧化二者共同作用的结果。     

高镁镍渣-磷石膏基复合胶凝材料的制备与性能评价

采用机械研磨的方式将高镁镍渣（HMNS）和磷石膏（PG）筛分至不同粒度，评价了掺不同粒度高镁镍渣和磷石膏复合胶凝材料的力学性能，并对强度形成机制进行了分析。评价了各种配比下浆体的抗压强度和体积稳定性，并分析了其作用机制。试验表明：以HMNS∶PG∶富钙硅质材料ZL=5.4∶3.6∶1配比制得试样的28 d抗压强度为4.43 MPa；室温环境下养护56 d，SP6线性收缩为1.02×10-3 mm/mm，体积稳定性优良；水化产物Ca(OH)2更少，Ca（OH）2与HMNS-PG体系反应生成了CSH凝胶和AFt，结构更为稳定。